Introducing the questions you contacted Connection

We would like to introduce the contents of inquiries regarding the availability of plating, materials and sizes.

  01 01

Q. Is it possible to express a pattern like a camouflage pattern on a metal plate?

A. It is possible to express camouflage patterns and various other patterns on the metal plate.

  02 02  

Q. Is it possible to perform the following surface treatment and film formation on Prime Grade silicon wafers?

  1. Hydrogen fluoride cleaning

  2. ALD treatment (Al2O3 single side 5-10nm)

A. We have confirmed the content of the consultation.

If the wafer size is about 3 inches, we can handle up to ALD processing.

Al2O3 film formation by ALD is planned to be a film formation using a combination of TMA (trimethylaluminum) and water, but a film formation test using high concentration ozone instead of water is also available.

  03 03  

Q. Is it possible to handle beryllium copper material procurement, machining, surface polishing, buffing, and tin plating?

A. I checked the drawing.

We can handle everything from material arrangement, machining, surface polishing, buffing, and tin plating.

  04  

Q. Is it possible to plate ABS resin?

A. It is possible to plate ABS resin. Please tell us if there are any specifications for the required characteristics (design, functionality, etc.) and color tone.

  05 05  

Q. The product is a hook pin with nickel plating on the iron material. Is it possible to express the old beauty color (dull brass color)?

A. It is possible to express an old-fashioned color (dull brass color) on a nickel-plated product.

  06 06  

Q. I use trichlorethylene (toluene) for cleaning, but the material may become cloudy or eroded.

What are the possible causes?

A. Trichlorethylene (toluene) is hydrolyzed to produce hydrochloric acid, which is thought to be the cause.

It is necessary to devise so that water does not enter trichlorethylene.

  07 07  

Q. I would like to change the hydrophobicity of fluororesin to hydrophilicity. Is this possible?

A. It is possible to make fluororesin hydrophilic by treating it with a special treatment liquid.

Since it can be made hydrophilic, it is possible to write characters such as magic on fluororesin and join it.

  08 08  

Q. Regarding low-temperature black chromium products processed by other companies, when hexavalent chromium is analyzed, it exceeds the allowable value of the RoHS Directive.

Is there a way to reduce the content of hexavalent chromium?

A. Regarding the hexavalent chromium content of low-temperature black chromium, it is possible to reduce the content with a special treatment liquid.

We would appreciate it if you could actually process it and evaluate it.

  09 09  

Q. Is it possible to process S45C with Penetron treatment (polymer tungsten coating treatment) (discharge hardening treatment) for a part of the product?

A. Only the specified part can be treated with Penetron for the specified material.

  Ten  

Q. Is it possible to apply electroless nickel plating + Teflon coating to the roll for antistatic purposes?

A. Both electroless nickel and Teflon coating for antistatic purposes are available.

  11  

Q. We are considering surface treatment for joining Teflon pipes.

Is it possible to improve the surface so that Teflon pipes can be joined?

A. There is a treatment that can be done by modifying the surface of the Teflon pipe to make it hydrophilic.

Please let us know the product size etc. and we will give you a quote.

  12  

Q. Is electroless nickel matte black compatible with a flat plate of aluminum material (A7075) of about 350 x 350 mm?

A. Regarding inquiries, we can handle both size and processing content.

We will give you a clear answer if you give us detailed drawings.

  13  

Q. Titanium plate 1 type (TP270) / 2 type (TP340) is not specified, but is it possible to prepare a plate of t0.5, 210 mm ✕ 297 mm?

A. Titanium plate 1 type (TP270) / 2 type (TP340) can be handled from material arrangement.

  14  

Q. Is it possible to arrange stainless steel materials, laser cutting, barrel polishing, and bending?

A. We can handle everything from material procurement, laser cutting, barrel polishing, and bending to the materials you consult with.

  15  

Q. Is ELP-Fe / Ni-P5 (Black) compatible with S45C?

The size is 750 x 640 t15 mm.

A. S45C (carbon steel for machine structure) can be supported by ELP-Fe / Ni-P5 (Black) black electroless nickel 5 μm or more.

There is no problem in terms of size.

  16  

Q. I would like to apply platinum plating (Pt plating) 1 μm treatment to titanium. Is this possible?

A. Titanium material can be plated with platinum, but the following points should be noted.

・ Please use pure Ti for Ti.

-The finish will be matte.

-Since it is a rack type (hanging) plating, rack marks (chucking marks) will occur.

The plating around the chucking part becomes thin or unattached, so the corrosion resistance is partially reduced.

  17  

Q. Is it possible to partially coat the two materials of titanium with iridium oxide?

A. Iridium oxide coating on titanium for inquiries (only for designated parts) is available.

  18  

Q. I would like to black-dye stainless steel. Is this possible?

A. Stainless steel can be dyed black.

The reaction differs depending on the SUS count, and 304, 303, and 316 are part numbers that are easy to react.

Other product numbers may not respond, or may have a dull or brownish color, so we would appreciate it if you could make a prototype first.

  19  

Q. I was told by a local plating shop that zinc die casting cannot be re-plated.

Is it possible to re-plat (preferably chrome-plat) zinc die-cast?

A. It is possible to re-plat to zinc die-cast.

We can process in the process of plating peeling → polishing → copper plating → nickel plating → chrome plating.

Since it is re-plated, it will be more expensive than purchasing a new one.

If you can buy a new one, we recommend that one in terms of cost.

  20  

Q. Is it possible to handle everything from material procurement to processing and precision cleaning of the machinable ceramics "Shapal Hi Msoft"?

A. Machinable ceramics "Shapal Hi Msoft" is a product of Tokuyama Corporation, but from material purchasing to machining,

We can handle up to precision cleaning.

  twenty one  

Q. The wooden box for importing and exporting products has been partially damaged. Is it possible to repair it?

A. Our cooperating manufacturers can handle both manufacturing and repair of wooden boxes.

In addition, fumigated wood is always in stock, so there is no problem with export.

  twenty two  

Q. I am considering Almer processing (Al-Fe). Is it possible to handle it?

A. It depends on the size and quantity, but we can handle it.

If you can keep the drawings etc., we will check whether it can be processed.

  twenty three  

Q. Regarding hot-dip aluminum plating, what is the film hardness?

A. Regarding the film hardness of molten aluminum plating, the film hardness of the Al-Fe alloy part is about Hv900.

  twenty four  

Q. I am considering Almer processing, but I am concerned about distortion.

Please tell me the processing temperature.

A. The processing temperature for Almer processing is around 700 ° C.

Welds and thin products will be distorted.

  twenty four  

Q. Is it possible to treat S45C with Aluminize α?

A. Aluminize α processing is available.

If you contact us about the product size and quantity, we will confirm the availability.

  twenty five  

Q. Is it possible to treat Ti material with iridium oxide (1 μm or more)?

A. Processing is available.

If you contact us about the product size and quantity, we will confirm the availability.

  26  

Q. We are considering rhodium plating 3 μm for iron material (carbon tool steel SK105).

Is it possible?

A. Rhodium plating on iron materials is possible, but 3 μm thick films are not.

The maximum is 0.3 μm.

In addition, it is necessary to apply nickel plating to the base.

We would appreciate it if you could consider it.

イメージ.jpg

Contact us

Please feel free to contact us by e-mail or phone for consultation on surface treatment (plating, coating, polishing, heat treatment, etc.).

Consultation and quotation are free.

Reception hours 9: 00-18: 00 Direct telephone 090-6819-5609