ノンクラック硬質クロムメッキ

Details of hard chrome plating (industrial chrome plating)

A hard chrome plating (industrial chrome plating) film is a film with a beautiful bluish silver-white color tone, and because it forms a passivation film in the atmosphere, it is a film that can maintain a beautiful color tone without discoloration.

Chromium plating is roughly divided into decorative and industrial use. According to JIS standards, film hardness of 750 HV or more and film thickness of 2 μm or more are for industrial use.

Chrome plating of 2 μm or more is used for industrial purposes because of its good wear resistance.

Excellent corrosion resistance

It is not easily corroded by acids other than hydrochloric acid and alkalis, and has excellent corrosion resistance.

High film hardness

Since the hardness of the hard chrome plating film is as high as HV750 or higher, it has excellent wear resistance compared to other metals.

断面観察

断面観察(クラックあり).jpg
断面観察(クラックフリー).png
  一般的な硬質クロム断面             ノンクラック硬質クロム断面

 
ノンクラック硬質クロムめっき開発の目的

クロムめっきの割れが皮膜物性に与える影響として、成形フィルムへの転写、皮膜の剥がれ、耐食性の低下が挙げられます。クロムめっき皮膜にクラックが存在することで、腐食因子が毛細管現象により割れ目に浸透し、素材の腐食を引き起こします。

めっき皮膜にクラックが無ければこのような現象は起こらないため、クロムめっきの割れやピンホールを無くしたノンクラック硬質クロムを開発しました。

ノンクラック硬質クロムめっき皮膜硬度

硬質クロムめっきと言えばやはり皮膜の硬さが大きな特徴ではないでしょうか?

世の中にも実はクラックのないクロムめっきは存在しております。弊社との違いは何と言っても硬さです。

一般的なクラックフリーのクロムめっきの皮膜硬度HV500〜600程度

ノンクラック硬質クロムめっきの皮膜硬度HV750〜850程度ですので、日本工業規格(JIS H8615)をクリアした内容で対応可能です。

純チタンやチタン合金の部品で焼き付き(摩耗性)など困っていませんか?

純チタンやチタン合金は同種金属と焼付きを起こしやすく、摩耗性が劣るという欠点があります。

純チタン、チタン合金に硬質クロムめっきの対応可能です。

ロゴ.jpg

Connection Co., Ltd.

Please feel free to contact us for plating, coating, polishing, heat treatment, etc.

Consultations and quotations are free.

​4-202-5 Shizugaoka, Fukui City, Fukui Prefecture 910-3635 (Japan)

​Reception hours 9: 00-18: 00 

Direct phone 090-6819-5609

Science_edited.jpg